Gu Z, Alexandridis P: Drying of films formed by ordered poly (ethylene oxide)-poly (propylene oxide) block copolymer gels. Langmuir. 2005 Mar 1;21(5):1806-17.
The drying of hydrogel films formed by poly (ethylene oxide)-poly (propylene oxide) (PEO-PPO) block copolymers (Pluronic P105 and Pluronic L64) is investigated at various air relative humidity (RH) conditions in the range 11-94%. These amphiphilic block copolymers self-assemble to form a variety of ordered (lyotropic liquid crystalline) structures as the water content decreases. The amount of water lost increases linearly with the drying time initially (constant rate region, stage I). After this linear region, a falling rate is observed (stage II). The drying rate increases with decreasing RH, thus greatly shortening the drying time. A decrease of the initial film thickness or a decrease in the initial water content shortens the drying time; however, the drying mechanism remains the same. Analysis of the experimental data shows that the hydration level in the Pluronic hydrogel mainly determines the drying rate, rather than the type of ordered structure formed. Two distinct regions (liquid/gel and solid/crystalline) are observed in the drying isotherm for PEO-PPO block copolymers and homopolymer poly (ethylene glycol) s. A model for one-dimensional water diffusion is used to fit the experimental drying results at different RH, initial film thickness, and initial water content conditions. The model accounts for the shrinkage of the film during drying and for a water diffusion coefficient that is a function of the water concentration in the film. For the experimental conditions considered here, the Biot number (Bi) is less than unity and the drying is mainly limited by evaporation at the film surface. The diffusion model is used to obtain information for cases where Bi > 1. |
81(1,1,1,1) |