Ji Y, Ghosh K, Shu XZ, Li B, Sokolov JC, Prestwich GD, Clark RA, Rafailovich MH: Electrospun three-dimensional hyaluronic acid nanofibrous scaffolds. Biomaterials. 2006 Jul;27(20):3782-92. Epub 2006 Mar 23.
A three-dimensional (3D) hyaluronic acid (HA) nanofibrous scaffold was successfully fabricated to mimic the architecture of natural extracellular matrix (ECM) based on electrospinning. Thiolated HA derivative, 3,3'-dithiobis (propanoic dihydrazide)-modified HA (HA-DTPH), was synthesized and electrospun to form 3D nanofibrous scaffolds. In order to facilitate the fiber formation during electrospinning, Poly (ethylene oxide) (PEO) was added into the aqueous solution of HA-DTPH at an optimal weight ratio of 1:1. The electrospun HA-DTPH/PEO blend scaffold was subsequently cross-linked through poly (ethylene glycol)-diacrylate (PEGDA) mediated conjugate addition. PEO was then extracted in DI water to obtain an electrospun HA-DTPH nanofibrous scaffold. NIH 3T3 fibroblasts were seeded on fibronectin-adsorbed HA-DTPH nanofibrous scaffolds for 24h in vitro. Fluorescence microscopy and laser scanning confocal microscopy revealed that the 3T3 fibroblasts attached to the scaffold and spread, demonstrating an extended dendritic morphology within the scaffold, which suggests potential applications of HA-DTPH nanofibrous scaffolds in cell encapsulation and tissue regeneration. |
1(0,0,0,1) |